LC Materials Fiberglass Prepreg Listing |
|
|
|
|
|
|
LCM PRODUCT |
DESCRIPTION |
NOMINAL CURE TEMP F° (C°) / TIME |
COLOR |
APPLICATION |
MISC. |
|
LC-E320 |
Epoxy Prepreg |
250 (121) / 60 min. |
Cream |
Sandwich structures, laminates, radomes, antennas and structures requiring low dielectric constant |
Various colors & fabric styles available |
|
LC-E321 |
Flame Retardant Epoxy Prepreg |
250 (121) / 60 min. |
Cream |
Laminates, sandwich structures without use of additional film adhesive |
Various colors & fabric styles available Meets FAR 25.853 |
|
LC-E321ET |
Flame Retardant Epoxy Prepreg Elevated Tg vs LC-E321 |
250 (121) / 60 min. |
Cream |
Laminates, sandwich structures without use of additional film adhesive |
Various colors & fabric styles available
Meets FAR 25.853 |
|
LC-E321FR |
Flame Retardant Epoxy Prepreg
Additional FR vs LC-E321 |
250 (121) / 60 min. |
Cream |
Laminates, sandwich structures without use of additional film adhesive |
Various colors & fabric styles available
Meets FAR 25.853 |
|
LC-E321QC |
Flame Retardant Epoxy Prepreg
Accelerated Cure Cycle vs LC-E321 |
260 (126) / 20 min. |
Cream |
Laminates, sandwich structures without use of additional film adhesive |
Various colors & fabric styles available
Meets FAR 25.853 |
|
LC-E322 |
Toughened Flame Retardant Epoxy Prepreg |
250 (121) / 60 min. |
Cream |
High toughness for laminates, sandwich structures without use of additional film adhesive, high impact areas |
Various colors & fabric styles available
Meets FAR 25.853 |
|
LC-E323 |
Toughened Clear Epoxy Prepreg |
250 (121) / 60 min. |
Clear |
Automotive, sporting goods requiring optically clear finish |
FR version available |
|
LC-E324 |
Toughened Flame Retardant Epoxy Prepreg Low Temp Processing |
175 (79) / 360 min. |
Cream |
High toughness for wood, foam, bolsa construction, laminates, sandwich structures without use of additional film adhesive |
Various colors & fabric styles available
Meets FAR 25.853 |
|
LC-E325 |
Toughened Flame RetardantEpoxy Prepreg |
250 (121) / 60 min. |
Cream |
Laminates, sandwich structures without use of additional film adhesive, high impact areas |
Various colors & fabric styles available |
|
LC-E328 |
Low Exotherm Epoxy Prepreg |
250 (121) / 60 min.
See data sheet for additional cure cycle(s) |
Black |
Laminates, multi-ply structural parts,thick cross sections |
Various cure cycles pending part thickness. |
|
LC-E333 |
Toughened Clear Epoxy Prepreg Low Temp Processing |
175 (79) / 360 min. |
Clear |
High toughness for wood, foam, bolsa construction laminates, sandwich structures without use of additional film adhesive |
Various fabric styles available. |
|
LC-E334 |
High Temperature Epoxy Prepreg |
350 (176) / 60 min. |
Cream |
High temperature laminates, sandwich structures, multi-ply structural parts, |
Various colors & fabric styles available.FR version available |
|
LC-E342PG |
Toughened Flame Retardant Prepreg |
275 (135) / 90 min. |
Cream |
Commercial aircraft interiors requiring FST/OSU compliance |
Various colors & fabric styles available.FAR 25.853 |
|
LC-E345T |
Variable Temperature Cure Epoxy Tooling Prepreg |
See data sheet for cure cycle & post cure |
Black |
Tooling, Caul sheets requiring high quality surface finish |
Low temp initial cure with high temp capabilities after post cure |
|
LC-C347 |
Cynate Ester Prepreg |
250 (121) / 180 min. |
Amber |
High service temperature parts requiring low dielectric constant |
Elevated post cure available for higher Tg requirements |