| LC Materials Film Adhesives Listing | ||||||||||
| LCM PRODUCT | DESCRIPTION | NOMINAL CURE TEMP F° (C°) / TIME | COLOR | APPLICATION | MISC. | |||||
| LC-E220 | Modified Epoxy | 250°(121°) / 60 min | Cream | Bonding metals, composites, various substrates, honeycomb structures. Radomes, Solar Arrays, Antennas | ||||||
| LC-E221 | Flame Retardant Modified Epoxy | 250° (121°) / 60 min | Cream | Bonding metals, composites, various substrates, honeycomb structures | FAR 25.853a | |||||
| LC-E221ET | Flame Retardant Modified Epoxy | 250°(121°) / 60 min | Cream | Bonding metals, composites, various substrates, honeycomb structures | FAR 25.853a Elevated Tg vs. LC-E221 | |||||
| LC-E221QC | Flame Retardant Modified Epoxy Quick Cure | 260° (126°) / 20 min | Cream | Bonding metals, composites, misc. substrates, honeycomb structures, with reduced process time |
FAR 25.853a Accelerated Cure Cycle vs LC-E221 |
|||||
| LC-E222 | Toughened Flame Retardant Modified Epoxy | 250° (121°) / 20 min | Cream | Bonding metals, composites, various substrates, honeycomb structures. Excellent for high impact areas | FAR 25.853a | |||||
| LC-E223 | Modified Epoxy / Optically Clear | 250° (121°) / 60 min | Clear/Black Tint | Cosmetic parts requiring high clarity | ||||||
| LC-E224 | Toughened Flame Retardant Modified Epoxy Low Temp Cure | 175°(79°) / 360 min | Cream | Bonding metals, composites, various substrates, honeycomb structures. Excellent for high impact areas | FAR 25.853a | |||||
| LC-E225 | Toughened Modified Epoxy | 250°(121°) / 60 min | Cream | Bonding metals, composites, various substrates, honeycomb structures. Excellent for high impact areas | ||||||
| LC-E227 | Modified Epoxy / Elevated Temperature Aluminum Filled | 350° (176°) / 60 min | Grey | Bonding metal to metalExcellent for continuous 350° (176°). service temp | ||||||
| LC-E229 | Flame Retardant Modified Epoxy | 250°(121°) / 60 min | Cream | Bonding metal(s), composites, misc. substrates, honeycomb structures |
FAR 25.853a MMM-A-132B |
|||||
| LC-E232 | Modified Epoxy Core Splice | 250° (121°) / 60 min | Blue Tint | Core splice and edge close outExpansion ratio of 2-3 times | FR version available | |||||
| LC-E233 | Modified Epoxy / Optically Clear Low Temp Cure | 175° (79°) / 360 min | Clear/Black Tint | Cosmetic parts requiring high clarity | FR version available | |||||
| LC-E234FA | Modified Epoxy / Elevated Temperature | 350° (176°) / 60 min | Cream | Bonding honeycomb structures requiring elevated service temperature | Film adhesive available | |||||
| LC-E237/8G | Flame Retardant Modified Epoxy Surfacing Film | 250°(121°) / 60 min | Grey | Flat or contour parts requiring excellent surface finish 350°(176°) curing available | Various colors available FAR 25.853a | |||||
| LC-E239 | Modified Epoxy / Optically Clear | 250° (121°) / 60 min | Clear/Black Tint | Automotive & Sporting Goods requiring high clarityCuring from 150° (65°) to 390° (198°) | FR version available | |||||
| Notes: |
| - Various colors available upon request - Film adhesives can be supplied supported or unsupported with various substrates - Additional cure cycles available - Various weights available upon request - Low, medium and high tack available in most cases |